SOME PHYSICAL AND MECHANICAL PROPERTIES OF PARTICLE BOARDS PRODUCED FROM INDUSTRIAL WOOD CHIPS AND SCOTS PINE (Pines sylvestris) CONES
Küçük Resim Yok
Tarih
2025
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Univ Bio-Bio
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
This study investigated the potential use of Scots pine cones as an alternative raw material to larch wood chips for particle board production. Due to the increasing scarcity of forest resources, exploring alternative raw material for the forest industry has gained importance in in recent years. Particle boards were produced in laboratory conditions by blending industrial wood chips with Scots pine cones in varying proportions (25 %, 50 %, 75 % and 100 %) and usingr urea formaldehyde glue. The adhesice mixture contained 55 % urea formaldehyde glue and 33 % ammonium chloride as a hardener. Te production parameters included a press temperature of 150 degrees C, a press time was 7 minutes, and a press pressure of 2,4 MPa to 2,6 MPa. The resulting boards had a thickness of 16 mm and a density ranging from 730 kg/m3 to 740 kg/m3. Tests for thickness iswelling, water absorption, , bending strength, modulus of elasticity and tensile strength perpendicular to the surface were conducted. Results showed that the physical and mechanical properties of the boards containing up to 25 % Scots pine cone met the required standards.
Açıklama
Anahtar Kelimeler
Larch chip, mechanical properties, particle board, physical properties, pinus sylvestris, raw material, scots pine cone, wood chips
Kaynak
Maderas-Ciencia Y Tecnologia
WoS Q Değeri
Q2
Scopus Q Değeri
Q2
Cilt
27