Experimental and Statistical Study on Machinability of the Composite Materials with Metal Matrix Al/B4C/Graphite
Yükleniyor...
Dosyalar
Tarih
2017
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, four types of Al/B4C/Graphite metal matrix composites (MMCs) were produced by means of a hot-pressing technique with reinforcement elements, B4C 8 wt pct and graphite (nickel coated) 0, 3, 5, and 7 wt pct. Machinability tests of MMC materials thus produced were conducted using four different cutting speeds (100, 140, 180, and 220 m/min), three different feed rates (0.1, 0.15, and 0.20 mm/rev), and a fixed cutting depth (0.5 mm), and the effects of the cutting parameters on the average surface roughness were examined. After the machinability tests, the height of the built-up edge (BUE) formed on the cutting tools related to the cutting speed and feed rate was measured. The test results were examined by designing a matrix according to the full factorial design and the average surface roughness, and the most important factors leading to formation of the BUE were analyzed by the analysis of variance (ANOVA). As a result of analysis, it was found that the lowest surface roughness value was with 7 wt pct graphite MMC material, while the highest was without graphite powder. Based on the statistical analysis results, it was observed that the most important factor affecting average surface roughness was the type of MMC material, the second most effective factor was the feed rate, and the least effective factor was the cutting speed. Furthermore, it was found that the most important factor affecting the formation of the BUE was the type of MMC material, the second most effective factor was the cutting speed, and the least effective factor was the feed rate.
Açıklama
NAS, Engin/0000-0002-4828-9240
WOS: 000408884300055
WOS: 000408884300055
Anahtar Kelimeler
Kaynak
Metallurgical And Materials Transactions A-Physical Metallurgy And Materials Science
WoS Q Değeri
Q2
Scopus Q Değeri
Q1
Cilt
48A
Sayı
10