Fiber-Reinforced Lightweight Calcium Aluminate Cement-Based Concrete: Effect of Exposure to Elevated Temperatures
Küçük Resim Yok
Tarih
2023
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Mdpi
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Calcium aluminate cements (CACs) are a group of rapid-hardening hydraulic binders with a higher aluminum composition and lower ecological footprint compared to their ordinary Portland cement (CEM) counterparts. CACs are commonly known to have higher thermo-durability properties but have previously been observed to experience a major strength loss over time when exposed to thermal and humidity conditions due to the chemical conversion of their natural hydrated products. To address this, in this study, silica fume is added to induce a different hydration phase path suggested by previous studies and utilized in conjunction with fiber-reinforced lightweight pumice to produce lightweight concrete. To closely evaluate the performance of the produced samples with CAC compared to CEM, two different types of cement (CEM and CAC) with different proportions of pumice and crushed stone aggregate at temperatures between 200 and 1000 degrees C were tested. In this context, sieve analysis, bulk density, flowability, compressive and flexural strength, ultrasonic pulse velocity and weight loss of the different mixes were determined. The results of this study point to the better mechanical properties of CAC samples produced with pumice aggregates (compared to crushed stone) when samples are exposed to high temperatures. As a result, it is found that CACs perform better than CEM samples with lightweight pumice at elevated temperatures, showing the suitability of producing lightweight thermal-resistant CAC-based concretes.
Açıklama
Anahtar Kelimeler
calcium aluminate cement (CAC), lightweight concrete, pumice, thermal performance, silica fume, Silica Fume, Strength, Microstructure, Conversion, Powder
Kaynak
Sustainability
WoS Q Değeri
Q2
Scopus Q Değeri
Q1
Cilt
15
Sayı
6