Synthesis and Optoelectronic Properties of Pyrite (FeS2) Nanocrystals Thin Films for Photovoltaic Applications
Küçük Resim Yok
Tarih
2013
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Amer Scientific Publishers
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Nanocrystal (NCs) pyrite FeS2 were synthesized on indium thin oxide (ITO) substrate by using thermal reaction of iron-oleyamine complexes with sulfur in olayamine. The structural and optical characterizations of FeS2 NCs were investigated and the effect of annealing temperature on thin film properties was discussed. The Scanning Electron Microscope (SEM) images shows that FeS2 films have between 25 nm and 100 nm diameter and as the annealing temperature on the thin film increased, the particle size increased. The absorption spectrums show that FeS2 NCs have direct band gap between 1.27 and 2.04 eV which is much higher than that of bulk FeS2 (0.95 eV). The changes of particle size can be attributed to the different interactions of surface energy and interface energy at different annealing temperatures. Current-Voltage characteristics show that NCs FeS2 has high conductivity and it was found that when annealing temperature of thin films increases, conductivity decreases. The surface photo voltage (SPVs) of FeS2 films was studied to explore their potential in photovoltaic application as well.
Açıklama
WOS: 000323356300005
Anahtar Kelimeler
Pyrite (FeS2), Nanocrystal Thin Films, Photovoltaic, Surface Photo Voltage (SPV)
Kaynak
Journal Of Nanoelectronics And Optoelectronics
WoS Q Değeri
Q4
Scopus Q Değeri
N/A
Cilt
8
Sayı
3