The Influence of Particle Size and Reinforcement Rate of B4C on Mechanical and Microstructure Properties of Al-B4C Composites

Yükleniyor...
Küçük Resim

Tarih

2020

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

Erişim Hakkı

info:eu-repo/semantics/openAccess

Özet

In this study, Al-B4C composites were produced with various particle sizes (B4C: 3.5 and 20 µm) andreinforcement rates (B4C%: 1, 3, 6, 9, 12, 15, 30%) by the powder metallurgy method. The apparent density,compressive strength, and Vickers hardness of the composites were determined by Archimedes’ density meter,universal test machine, and micro Vickers hardness measurement device, respectively. The phase andmicrostructural analysis of the fabricated composites were analyzed using an X-ray diffraction device andscanning electron microscope, respectively. From the test results, the highest micro Vickers hardness (68.8 HV),apparent density (2.61 g/cm3), compressive strength (242 MPa), and minimum porosity (1.4%) were determinedat 3.5 µm particle size and 30% reinforcement rate of B4C. The enhancement in Vickers hardness andcompressive strength of Al-30%B4C composite was detected as +129.3% and +165.9% compared with purealuminum.

Açıklama

Anahtar Kelimeler

Kaynak

Düzce Üniversitesi Bilim ve Teknoloji Dergisi

WoS Q Değeri

Scopus Q Değeri

Cilt

8

Sayı

3

Künye