Strontium-Modified TiO2 Nanotubes for Efficient Photodegradation of Formic Acid
Küçük Resim Yok
Tarih
2025
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer Heidelberg
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
This study explores the enhancement of photocatalytic activity in one-dimensional TiO2 nanotubes (TiNT) through strontium (Sr) doping, using the incipient impregnation method to introduce Sr concentrations ranging from 0.2 to 1.0 wt%. The photocatalytic performance of the resulting xSr-TiNT composites was evaluated by examining the degradation of formic acid under UV irradiation. The materials were characterized using N2 physisorption, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV-vis, Raman spectroscopy, photoluminescence (PL), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The effective surface area was determined by XPS, revealing a significant increase in surface area with Sr loading, which correlates with enhanced photocatalytic performance. This enhancement in surface area is in agreement with the observed expansion of the unit cell volume in presence of Sr. Results show that a small amount of Sr (0.2 wt%) enhances the generation of oxygen vacancies and Ti3+ species, leading to increased photocatalytic activity. The degradation followed the Langmuir-Hinshelwood model, with the highest degradation rate observed at 0.8 wt% Sr, showing a 3.36-fold increase compared to pristine TiNT. At higher Sr concentrations, the proportion of oxygen vacancies and Ti3+ defects decreased due to the formation of Ti-O-Sr moieties. Additionally, the polarization effect induced by Sr doping improved charge separation, reducing electron-hole recombination and further enhancing photocatalytic efficiency. These findings emphasize the critical role of Sr concentration, effective surface area, and unit cell volume expansion in tuning the photocatalytic properties of TiO2 nanotubes, with an optimum Sr loading of 0.8 wt% leading to improved photocatalytic activity.
Açıklama
Anahtar Kelimeler
Strontium species, Oxygen defects, Nanotubes, Kinetics, Photodegradation
Kaynak
Arabian Journal For Scienceand Engineering
WoS Q Değeri
Q2
Scopus Q Değeri
Q1