THE EFFECTS OF USING PERMEABLE FORMWORK ON CONCRETE MATURITY
Küçük Resim Yok
Tarih
2009
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Gazi Univ, Fac Engineering Architecture
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
The aim of this study is to investigate the effects of using permeable formwork on concrete maturity. For this purpose, four curtain wall formworks having 120 cm height, 70 cm with and 20 cm thickness; were prepared. As a surface material one Black pine and three plywoods formworks were used. Drainage channels and holes were cut on the surfaces of two of plywoods formworks and the surfaces of these formworks were covered with different geotextile liners. The other polywood formwork selected as reference sample any processing has done. Maturity measuring apparatuses were placed on the geometric centre of the curtain wall formworks. C30 concrete were cast into the prepared formworks and compressed with a vibrator. In addition, 16 number of concrete samples having 15x15x15 cm dimensions were prepared. The maturity measuring device was placed into the one of these samples. And the other samples were waited into the curing pool and the compressive strength of the samples was determined at the 1(st), 3(rd), 7(th), 14(th), and 28(th) days respectively. As a result, it is seen that, maturity index of the concrete cast into the permeable formworks is high as 11% than the black pine and plywood formworks and the concrete cast into the permeable formworks were gained earlier strength. Besides, it is seen that, concrete maturity may be accelerated with using permeable formworks.
Açıklama
WOS: 000274618300018
Anahtar Kelimeler
Permeable formwork, maturity, compressive strength, concrete
Kaynak
Journal Of The Faculty Of Engineering And Architecture Of Gazi University
WoS Q Değeri
N/A
Scopus Q Değeri
Cilt
24
Sayı
4