Investigation of the effect of FDM process parameters on mechanical properties of 3D printed PA12 samples using Taguchi method
Küçük Resim Yok
Tarih
2023
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
SAGE Publications Ltd
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
This study investigated the effects of FDM (Fused Deposition Modeling) process parameters on mechanical properties (tensile strength, elongation, and impact strength) of 3D (three-dimensional) printed PA12 (Polyamide12) samples using Taguchi method. In the experimental design (L<inf>8</inf>), four different layer thickness (0.1, 0.15, 0.2, 0.25 mm), extruder temperature (250 and 260°C), filling structure (Rectilinear and Full Honeycomb), and occupancy rate (25 and 50%) were determined. The tensile and impact strength test samples were printed with the FDM method. Tensile and impact strength of the test samples were carried out according to ISO 527 and ISO 180 test standards. The findings obtained from tests were analyzed and compared. As a result, the layer thickness is most effective factor for enhance the mechanical properties instead extruder temperature, occupancy rate, and filling structure. The optimum tensile strength of determined for process parameters (layer thickness, occupancy rates, filling structures and extruder temperature) were 0.25 mm, 50%, Rectilinear, and 250°C, respectively. The optimum impact strength of determined for process parameters (layer thickness, occupancy rates, extruder temperature, and filling structures) were 0.25 mm, 50%, 250°C, and Rectilinear, respectively. PA12 filament material can be used to printing for sleeve bearing due to their mechanical properties. It can be used in the production of many machine parts and components due to its tensile strength, impact strength resistance and damping properties. © 2022 Elsevier B.V., All rights reserved.
Açıklama
Anahtar Kelimeler
Fdm, Impact Strength, Mechanical Properties, Pa12, Taguchi, Tensile Strength, Filling, Fused Deposition Modeling, Impact Strength, Structural Properties, Taguchi Methods, Layer Thickness, Modeling Process, Occupancy Rate, Poly-amide 12, Process Parameters, Taguchi, Taguchi's Methods, Tensile Elongation, Tensile Impact, Test Samples, Tensile Strength
Kaynak
Journal of Thermoplastic Composite Materials
WoS Q Değeri
Scopus Q Değeri
Q1
Cilt
36
Sayı
1