Application Parameters of Water Transfer Printing on Wood-based Panel Surfaces
Yükleniyor...
Dosyalar
Tarih
2023
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
North Carolina State University
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Optimum application values of the Water Transfer Printing (WTP) technique were determined on various wood-based panel surfaces. For this purpose, 8-mm-thick, glossy white, acrylic-coated medium-density fiberboard (MDF) panels (high gloss panels), polyvinyl chloride (PVC)-coated MDF panels, MDF Lam ready-to-use panels, and cellulosic, polyurethane, acrylic, and water-based paint applied MDF panels were used. An automatic immersion system with pool was designed and produced. A 30-?m-thick carbon patterned WTP film was applied on sample panel surfaces prepared with the help of this device at four immersion angles (0º, 15º, 30º, and 45º), four immersion speeds (50 cm/min, 100 cm/min, 150 cm/min, and 200 cm/min), and four immersion times (5 to 10 s, 20 to 30 s, 50 to 60 s, and 80 to 90 s). The optimum parameters of the WTP technique regarding the temperature and relative humidity of the application environment, water temperature, laying method, dissolution time, amount of activator, spray gun angle and tip clearance, air pressure, as well as immersion angle, speed, and time were determined using the measurement and observation method. According to the optimum parameters obtained in the study, the WTP technique was successfully applied to all wood-based panel surfaces. © 2023, North Carolina State University. All rights reserved.
Açıklama
Anahtar Kelimeler
Coatings, Hydro dipping, Hydrographics, Water transfer printing, Wood-based panels, Chlorine compounds, Wood, Hydro dipping, Hydrographic, Immersion angle, Medium density fiberboard panels, Panel surfaces, Printing techniques, Transfer printing, Water transfer printing, Water transfers, Wood-based panels, Polyvinyl chlorides, Chlorine Compounds, Panels, Parameters, Submersion, Surfaces, Transfer Printing, Water, Wood
Kaynak
BioResources
WoS Q Değeri
Scopus Q Değeri
Q3
Cilt
18
Sayı
1