dc.description.abstractIn this study, screw withdrawal strength of solid wood material and laminated veneer lumber were determined according to TS EN 13446. Experiments were made on tangential surface and radial surface of solid wood material. Experiments were made on flatwise and edgewise directions of laminated veneer lumber. LVLs were produced from poplar and beech rotary peeled veneers using phenol formaldehyde adhesive. A half of the test samples were tested in air dried condition, and other half were tested after saturated with water. According to obtained findings, it was determined that screw withdrawal strength of the tangential surface of the solid wood materials was higher than that of radial surface. The highest screw withdrawal strength was measured on tangential surface of the beech solid wood material. The strength of laminated veneer lumber produced from poplar was higher than that of solid poplar. However, the strength of laminated veneer lumber produced from beech was lower than that of solid beech wood. In addition, the strength of all samples which were saturated with water was determined lower than that of air dried samples.
dc.description.abstractBu çalışmada, masif ağaç malzeme ve tabakalı kaplama kerestenin vida tutma direnci TS EN 13446’ya göre belirlenmiş ve karşılaştırılmıştır. Denemeler masif ağaç malzemelerde teğet yüzeylerde ve radyal yüzeylerde yapılmıştır. Tabakalı kaplama kerestelerde ise üst yüzeyde ve yan yüzeyde yapılmıştır. Tabakalı kaplama keresteler kayın ve kavak soyma kaplamalarından, fenol formaldehit tutkalı kullanılarak üretilmiştir. Test örneklerinin yarısı hava kurusu hale diğer yarısı ise su ile doygun hale getirildikten sonra test edilmiştir. Elde edilen bulgulara göre; masif ağaç malzemelerin teğet yüzeylerde vida tutma direncinin radyal yüzeylerden yüksek olduğu belirlenmiştir. En yüksek vida tutma direnci masif kayın da teğet yüzeyde ölçülmüştür. Kavaktan elde edilen tabakalı kaplama kerestenin vida tutma direnci masif kavaktan daha yüksek ölçülmüştür. Ancak, kayından elde edilen masif ağaç malzemenin vida tutma direnci kayından elde edilen tabakalı kaplama keresteye göre daha yüksek ölçülmüştür. Ayrıca su ile doygun hale getirilen örneklerin tamamının vida tutma direnci hava kurusu örneklerden daha düşük ölçülmüştür.
dc.identifier.dergiparkDergiPark: 288767
dc.identifier.endpage22
dc.identifier.issn2148-7871
dc.identifier.issn2148-7855
dc.identifier.issue2
dc.identifier.startpage14
dc.identifier.urihttps://dergipark.org.tr/tr/download/article-file/271950
dc.identifier.urihttps://dergipark.org.tr/tr/pub/duzceod/issue/4819/288767
dc.identifier.urihttps://hdl.handle.net/20.500.12684/16434
dc.identifier.volume9
dc.language.isoen
dc.publisherDüzce Üniversitesi
dc.relation.ispartofDüzce Üniversitesi Orman Fakültesi Ormancılık Dergisi
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_20241228
dc.subjectLaminated veneer lumber
dc.subjectLVL
dc.subjectlaminated wood material
dc.subjectscrew withdrawal strength
dc.subjectLVL
dc.subjectLamine ağaç malzeme
dc.subjectVida tutma direnci
dc.subjectFenol Formaldehid
dc.subjectTabakalı kaplama kereste
dc.titleA Comparative Study on Screw Withdrawal Strength of Solid Wood Material and Laminated Veneer Lumber
dc.title.alternativeMasif Ağaç Malzeme ve Tabakalı Kaplama Kerestenin Vida Tutma Direnci Üzerine Karşılaştırmalı Bir Çalışma
dc.typeArticle

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim
İsim:
Tam Metin / Full Text
Boyut:
219.02 KB
Biçim:
Adobe Portable Document Format
İndir

Koleksiyon

Düzce Üniversitesi Orman Fakültesi Ormancılık Dergisi Koleksiyonu