    Comparison of Micro- and Standard-Size Specimens in Evaluating the Flexural Properties of Scots Pine Wood
    (North Carolina State Univ Dept Wood & Paper Sci, 2016) Büyüksarı, Ümit; As, Nusret; Dündar, Türker; Sayan, Ezel
    The aim of this study was to investigate the flexural properties (bending strength and modulus of elasticity) of Scots pine wood (Pinus sylvestris L.) using micro-and standard-size test specimens. In the standard-and micro-size specimens, the average bending strengths were evaluated as 72.8 and 62.4 MPa, and the bending modulus of elasticity was 9917 and 2884 MPa, respectively. These results showed that the bending strength and modulus of elasticity values of the micro-size specimens were lower than those of the standard-size specimens. The statistically significant effects included the specimen size, individual trees, and the interactions of the specimen size and trees on the bending strength and modulus of elasticity. Furthermore, regression analyses indicated a positive linear regression between the flexural properties of the micro-and standard-size specimens. The results indicated that micro-size specimens can be used to estimate the flexural properties of Scots pine wood when obtaining standard-size specimens is not possible.
  • Küçük Resim
    Öğe
    Micro-Tensile and Compression Strength of Scots Pine Wood and Comparison with Standard-Size Test Results
    (Zagreb Univ, Fac Forestry, 2017) Büyüksarı, Ümit; As, Nusret; Dündar, Türker; Sayan, Ezel
    The goal of this study was to investigate the tensile and compression strength of Scots pine wood (Pinus sylvestris L.) using micro- and standard-sized test specimens. In the standard- and micro-sized specimens, tensile strength was evaluated as 76.9 MPa and 91.5 MPa and compression strength as 43.8 MPa and 36.3 MPa, respectively. The results showed that the compression strength of the micro- sized specimens was lower compared to the standard-sized specimens, while the tensile strength was higher in the micro- sized specimens. With the exception of the effect of specimen size and individual tree interaction on tensile strength, statistically significant effects were found for specimen size, individual trees and the interactions of the size and trees on the tensile and compression strength. Moreover, regression analyses indicated a positive linear regression between the strength of micro- and standard-sized specimens. Micro-sized specimens can be used to estimate the tensile and compression strength of Scots pine wood, when it is not possible to obtain standard-size specimens.
  • Küçük Resim
    Öğe
    Sarıçam odununun önemli mekanik özelliklerinin mikro-mekanik yöntemlerle belirlenmesi ve standart test sonuçları ile karşılaştırılması
    (Düzce Üniversitesi, 2016) Sayan, Ezel; Büyüksarı, Ümit
    Bu çalışmanın amacı mikro boyutlu Sarıçam odununun bazı mekanik özelliklerinin belirlenmesi ve mikro ve standart boyutlu örnekler arasındaki ilişkilerin ortaya konulmasıdır. Deneme ağaçları Bolu Orman Bölge Müdürlüğü'nden temin edilmiştir. Düzgün gövdeli 8 ağaç deneme ağacı olarak seçilmiştir. Her ağacın 0,30 m yüksekliğinden 3 m uzunluğunda tomruklar alınmış ve bu tomruklardan öz ortada olacak şekilde 6 cm kalınlığında keresteler alınmıştır. Mikro ve standart boyutlu test örnekleri bu kerestelerden hazırlanmıştır. Mikro ve standart boyutlardaki örnekler kullanılarak eğilme direnci, eğilmede elastikiyet modülü, liflere paralel çekme direnci ve basınç direnci değerleri tespit edilmiştir. Sarıçam odununda, standart ve mikro boyutlu örneklerde sırasıyla; eğilme direnci 72,8 N/mm2 ve 62,4 N/mm2, eğilmede elastikiyet modülü 9917,3 N/mm2 ve 2883,9 N/mm2, çekme direnci 76,9 N/mm2 ve 91,5 N/mm2 ve basınç direnci 43,8 N/mm2 ve 36,3 N/mm2 olarak bulunmuştur. Sonuçlar mikro boyutlu örneklerde eğilme direnci, elastikiyet modülü ve basınç direncinin daha düşük olduğunu, çekme direncinin ise standart boyutlu örneklerde daha yüksek olduğunu göstermiştir. Örnek boyutu- bireysel ağaç etkileşiminin çekme direnci üzerine etkisi hariç, örnek boyutu, bireysel ağaç ve örnek boyutu- bireysel ağaç etkileşiminin mekanik özellikler üzerine etkisinin istatistiki olarak anlamlı olduğu bulunmuştur. Regresyon analizi, standart ve mikro boyutlu örneklerin mekanik özellikleri arasında pozitif doğrusal ilişki olduğunu göstermiştir