Yazar "Bal, Bekir Cihad" seçeneğine göre listele
Listeleniyor 1 - 10 / 10
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe A Comparative Study on Screw Withdrawal Strength of Solid Wood Material and Laminated Veneer Lumber(Düzce Üniversitesi, 2013) Bal, Bekir Cihad; Özdemir, Ferhat; Altuntaş, ErtuğrulIn this study, screw withdrawal strength of solid wood material and laminated veneer lumber were determined according to TS EN 13446. Experiments were made on tangential surface and radial surface of solid wood material. Experiments were made on flatwise and edgewise directions of laminated veneer lumber. LVLs were produced from poplar and beech rotary peeled veneers using phenol formaldehyde adhesive. A half of the test samples were tested in air dried condition, and other half were tested after saturated with water. According to obtained findings, it was determined that screw withdrawal strength of the tangential surface of the solid wood materials was higher than that of radial surface. The highest screw withdrawal strength was measured on tangential surface of the beech solid wood material. The strength of laminated veneer lumber produced from poplar was higher than that of solid poplar. However, the strength of laminated veneer lumber produced from beech was lower than that of solid beech wood. In addition, the strength of all samples which were saturated with water was determined lower than that of air dried samples.Öğe A Comparative Study on the Coefficient of Thermal Expansion of Solid and Laminated Wood Materials(Düzce Üniversitesi, 2012) Bal, Bekir Cihad; Bektaş, İbrahim; Özdemir, FerhatIn this study, the coefficients of thermal expansion of solid wood and laminated wood materials preparedfrom beech (Fagus orientalis L.), poplar (Populus x euramericana I-214) and eucalyptus (Eucalyptus grandisW. Hill ex Maiden) species were determined. The experiments were made on the sapwood and heartwood ofsolid wood material, separately. Laminated wood materials were produced from 3 mm thickness rotary peeledveneer using UF (urea-formaldehyde) and PF (phenol-formaldehyde) adhesive. The tests were performedbetween -10 and +40 ºC temperature interval. In tangential direction, the lowest coefficient of thermal expansionwas measured on the poplar heartwood (1.88x10–5 ºC–1) and the highest coefficient of thermal expansion wasmeasured on the laminated wood made from eucalyptus used PF (4.66x10–5 ºC–1). The results showed thatlaminated materials produced from poplar wood has higher coefficient of thermal expansion than solid poplarwood. The differences between solid and laminated wood from the beech and eucalyptus weren’t statisticallysignificant.Öğe A Study on Differences in Fiber Morphology between Juvenile Wood and Mature Wood(Düzce Üniversitesi, 2012) Bal, Bekir CihadIn this study, the differences between juvenile wood and mature wood in fiber morphology on the samples prepared from cedar and eucalyptus were investigated. For this aim, cell length, cell width, lumen width, wall thicknesses were measured. The measurements were made on juvenile and mature wood, separately. In the maceration process, chlorite method was used. The differences between juvenile and mature wood were determined with T test. According to obtained findings, cell length of juvenile wood and mature wood of the cedar and eucalyptus were different significantly. Cell width and wall thickness of juvenile and mature wood in cedar were different significantly. But, the same differences were insignificant in eucalyptus.Öğe CNC Makineleri İle Ahşap Yüzeylerin Şekillendirilmesinde Çözünürlük Ve Tolerans Değerlerinin Önemi(Düzce Üniversitesi, 2023) Bostan, Tuncay; Bal, Bekir CihadBu çalışmanın amacı, CNC makineleri ile masif ahşap yüzeylerin şekillendirilmesinde çözünürlük ve tolerans değerlerinin etkisini belirlemektir. Önceki çalışmalarda, masif ahşap ve ahşap esaslı levhaların yüzeylerinin düz işlenmesinde oluşan yüzey pürüzlülüğü ve süre üzerine etki eden faktörler üzerine araştırmalar yapılmıştır. Önceki çalışmalarda ahşap yüzeylerin rölyef işlenmesinde çözünürlük ve toleransın etkisi ile ilgili herhangi bir çalışmaya ulaşılamamıştır. Denemelerde, 3 farklı tolerans değerinde ve 3 farklı çözünürlük değerinde çalışma planı oluşturulmuştur. CNC makinesi kesme parametreleri sabit tutulmuştur. Elde edilen verilere göre; çözünürlüğün artması ile genel olarak pürüzlülük değerinde (Ra) bir azalma olduğu belirlenmiştir. Fakat tolerans arttıkça yüzey pürüzlülüğünün arttığı görülmektedir. Çözünürlüğün süre ve enerji tüketimi üzerine çok fazla etki etmediği tespit edilmiştir. Toleransın ise enerji ve süreyi etkilediği ve tolerans artıkça enerji tüketimi ve süreninde azaldığı tespit edilmiştir. Genel olarak, enerji tüketimi ve süre arttıkça yüzey pürüzlülüğünün azaldığı söylenebilir.Öğe Lateral Nail Resistance of Plywood Produced from Different Tree Species(Düzce Üniversitesi, 2016) Bal, Bekir Cihad; Akçakaya, Elif; Gündeş, ZeynepMetal fasteners such as nails, screws and bolts are used as fasteners in the application of solid wood and wood based composite materials in wooden construction. The durability of the connection points is influenced by many factors. In this study, five ply plywood panels were produced using rotary veneers from beech, eucalyptus, poplar threes. The tree type of panels were produced as single species plywood (beech, eucalyptus and poplar), and two type of panels were produced as combination plywood (beech-eucalyptus-beech and beech-poplar- beech). The lateral nail resistance, deformation at maximum load, density and moisture content of the plywood panels were determined. The lateral nail resistance tests were conducted according to ASTM 1761. The ring nail was used in experiments. According to obtained data; the lateral nail resistance of beech, eucalyptus, poplar, beech-eucalyptus-beech and beech-poplar-beech plywood were 3296, 2757, 2134, 2964 ve 2489 N, respectively. According to obtained data; it was determined that three species and combination type affect significantly the lateral nail resistance of plywood.Öğe MOBİLYA ÜRETİMİ YAPILAN İŞ YERLERİNDE BECERİ EĞİTİMİNİN VERİMLİLİĞİ(Düzce Üniversitesi, 2017) Kolutek, Süleyman; Bal, Bekir CihadMobilya Sektörü Türkiye’de hızlıbüyüyen önemli sektörlerden birisidir. Son yıllarda yaklaşık olarak 2.4 milyardolar ihracat yapmaktadır. Bu ihracat miktarıyla, Türkiye en fazla mobilyaihraç eden ülkeler sıralamasında ilk 20’dedir. Ancak, son yıllarda, nbsp; mobilya sektörü yeterli sayıda kalifiyeeleman bulamamaktadır. Türkiye’de mobilya sektörü için öğrenci yetiştiren çoksayıda orta öğretim kurumları bulunmaktadır. Öğrenciler, bu kurumlarda verileneğitimin yanında, ayrıca, mobilya üretimi yapılan iş yerlerinde beceri eğitimide almaktadır. Bu çalışmada, beceri eğitiminin verimliliği anket yöntemiylearaştırılmıştır. Elde edilen verilere göre, beceri eğitimi alan öğrencilerinbüyük çoğunluğunun bu eğitimden memnun olduğu belirlenmiştir. Ayrıca,öğrencilerin, beceri eğitimi esnasında karşılaştıkları bazı sorunların olduğuda tespit edilmiştir.Öğe Relationship between Wood Physical Properties of English Oak (Quercus robur L.) and Soil Variables(Düzce Üniversitesi, 2016) Bektaş, İbrahim; Oruç, Suphi; Bal, Bekir Cihad; Kılıç Ak, AyşenurIn this study, some of the physical properties of the Q. robur L. wood, which is one of the most important tree species in the forestry of Turkey, and primary soil elements that have an effect during the formation of these properties, were investigated. For this purpose, test trees that were supplied from Dörtyol (Hatay) region were used. As a result of the tests, it was found that the annual ring width of Quercus robur L. wood was 2.1 mm, air dry density was 0.776 g/cm3, complete dry density was 0.721 g/cm3, volume-density value was 0.612 g/cm3, radial direction shrinking was 4.9%, tangential direction shrinking was 6.5%, volumetric shrinking was 11.4%, tangential direction swelling was 9.5%, radial direction swelling was 5.2% and volumetric swelling was found as 14.7%. According to obtained data, it was understood that it is rather suitable to grow Quercus robur L. wood in the soil characteristics of the habitat.Öğe SEDEF KAKMA SÜSLEMESİ ve GAZİANTEP BÖLGESİNDEKİ SEDEF KAKMA ATÖLYELERİNİN DURUMU ÜZERİNE BİR ARAŞTIRMA(Düzce Üniversitesi, 2017) Eser, Faruk; Bal, Bekir CihadGeçmişten günümüze, ahşap yüzeyleridaha güzel göstermek için farklı metotlar uygulanmıştır. Farklı renklerdeboyamak, oyarak farklı desenler işlemek veya farklı bazı malzemeleri ahşapyüzeylere yapıştırarak süslemek bu metotlardan bazılarıdır. Sedef kakma, gümüş,kalay, kurşun, alpaka tel, sedef, fildişi veya kemik gibi malzemelerin ahşapyüzeylere gömülmesi ile yapılan bir yüzey süsleme tekniğidir. Türkiye’de,Gaziantep bölgesinde yoğun olarak sedef kakmacılığı yapılmaktadır. Buçalışmada, Gaziantep bölgesinde sedef kakma atölyelerinin durumuaraştırılmıştır. Araştırma sonunda elde edilen bilgilere göre; geçmişte çoksayıda sedef kakma atölyesi faaliyet gösterirken, günümüzde bu sayının sonderece azaldığı belirlenmiştir. Bu sanatın, biten meslekler grubunda olduğu vebu alanda yeni usta yetişmediği belirlenmiştir. nbsp; nbsp;Öğe The Mechanical Properties of Heartwood and Sapwood of Flooded gum (Eucalyptus grandis) Grown in Karabucak, Turkey(Düzce Üniversitesi, 2013) Bal, Bekir Cihad; Bektaş, İbrahimcak, Turkey were determined. Mechanical properties, such as modulus of rupture, modulus of elasticity,impact bending strength, tension strength (perpendicular and parallel to grain), compression strength, shearstrength, and static hardness were measured. According to the test results the sapwood samples provided bettermechanical properties than the heartwood samples. It can be concluded that the lower mechanical properties ofthe heartwood samples were due to the presence of high proportion of juvenile wood in the heartwood.Öğe The Within-Tree Variation in Some Physical Properties in Eucalyptus Wood (Eucalyptus Grandis W. Hill ex Maiden) Grown in Karabucak Region(Düzce Üniversitesi, 2011) Bal, Bekir Cihad; Bektaş, İbrahim; Tutuş, Ahmet; Kaymakçı, AlperenBu çalışmada, E.grandis ağacında, radyal ve boyuna yönlerde, bazı fiziksel özelliklerdeki değişmelerincelenmiştir. Yoğunluk ile daralma miktarı arasındaki ilişki belirlenmiştir. Bu amaç için, örnekler sadece birağaçtan alınmıştır. Örnekler, gövdeden kabuktan öze doğru, dört eşit aralıklı noktadan ve gögüs seviyesindentaca doğru 8 eşit aralıklı noktadan alınmıştır. Bu örnekler üzerinde, taze hal rutubeti, tam kuru yoğunluk, hacimağırlıkdeğeri ve hacmen daralma miktarı belirlenmiştir ve en düşük ve en yüksek sonuçlar sırasıyla; %56-111,483-837 kg/m3, 440-722 kg/m3, %10.4-16.2 olarak ölçülmüştür. Ayrıca, regrasyon analizi hacmen daralmamiktarı ile tam kuru yoğunluk arasındaki pozitif-güçlü ilişkiyi ortaya koymuştur
