    The Effect of Weathering on Color and Glossiness Properties of Polyurethane-Modified Water-Based Varnish Layers Applied to Thermally Treated Ash Wood
    (North Carolina State University, 2025) Ulay, Goksel; Akter, Mete; Çakicier, Nevzat; Peker, Hüseyin; Ayata, Ümit; Atilgan, Abdi; Çiftçi, Seymen
    The effects of artificial weathering (168, 336, and 504 h) on the glossiness values and color parameters of varnished, polyurethane-modified ash wood were investigated. Samples included control samples without treatment and thermally treated samples under two different conditions (190 °C for 1.5 h and 212 °C for 2 h), all coated with a polyurethane-modified water-based varnish. In non-thermally treated and varnished samples, decreases in L* values were observed after weathering, while increases were noted in ho, C*, b*, and glossiness at 60° in both perpendicular and parallel directions to the fibers. After weathering, for samples thermally treated at 190 °C for 1.5 h and varnished, increases were observed in glossiness values at 20° and 60° in both directions, as well as in L*, b*, and ho values. Conversely, decreases were noted in a* and C* values. In samples thermally treated at 212 °C for 2 h and varnished, increases in a*, L*, ho, b*, and C* values were detected after weathering, whereas decreases were observed in glossiness at all angles (20° and 60°) in both directions. The ∆E* values showed a decreasing trend in non-thermally treated varnished samples after weathering, while an increase was observed in samples thermally treated at 212 °C for 2 h and varnished. © 2025 Elsevier B.V., All rights reserved.
  • Küçük Resim Yok
    Öğe
    THE EFFECTS OF WATER-BASED COLOR-PROTECTIVE BARRIERS ON NATURAL WOOD VENEER
    (Yildiz Technical Univ, 2019) Akter, Mete; Aytin, Ayhan; Konmaz, Carmelo Kağan
    In this study, the effects of water-based color-protective barriers on the color change of wooden veneers of various tree species were investigated. Wooden veneers of castanea, eucalyptus, and scots pine species which are widely used industrially - were selected for this purpose. The wood veneers were then divided into two groups and two separate top surface prescriptions were applied to each group. In the first group, only varnish was applied. On the second group, a water-based color-protecting barrier and varnish application was used, and a total of 6 variation test samples were prepared, with and without water color-protecting barriers applied to each tree type. Test samples were tested on both UVA and UVB lamps in the QUV aging device. It has been determined that water-based color-protective barriers do not show a significant color change in the applied parts, and that the veneer experiences discoloration in the areas not subjected to color-protective barriers. These results can be regarded as an industrially significant result, helping to overcome problems associated with the weathering of varnished surfaces.
  • Küçük Resim
    Öğe
    Su Bazlı Vernik Renk Bariyerinin, Doğal Ahşap Kaplamada Renk Değişimi ve Sertlik Üzerine Etkisi
    (2021) Aytin, Ayhan; Çakıcıer, Nevzat; Çiftçi, Seymen; Akter, Mete
    Dış hava koşulları kullanılmakta olan ağaç malzemenin çevresel faktörlerin etkisi ile kısa zamanda renk değişimine uğraması ve yüzeydeki koruyucu vernik katmanının deformasyonu önemli bir sorun olarak görülmektedir. Öte yandan üst yüzey işlemlerinde koruyucu katman yapmak üzere ekseriyetle solvent bazlı (SOB) maddelerin kullanılması insan ve çevre sağlığı bakımından birtakım sorunları da beraberinde getirmektedir. Günümüzde üretim süreçlerinde daha çok çevre dostu maddelerin kullanımı desteklenmekte, su bazlı vernik (SBV) sistemleri SOB sistemlere göre daha insan ve çevre dost olarak dikkati çekmektedir. Bu çalışmada dış tabakaları akçaağaç, okaliptüs ve meşe kaplamaları ile üretilmiş kontra tablaların yüzeyine iki farklı SBV sistemi; (1) özel bir astar kat ilave edilmiş modifiye su bazlı vernik (MSBV) ve (2) normal su bazlı vernik (NSBV) kullanılmıştır. Daha sonra 313 EL+ (UVA) ve UVB 313 EL(UVB) lambaları ile 144’er saat hızlandırılmış yaşlandırma (QUV) sonrası toplam renk değişimi(?E*) ve PS değerleri ölçülmüştür. Çalışma sonuçlarına göre ?E* en küçük MSBV sistemde 2.04, en yüksek NSBV’de 22.85 olarak ölçülmüştür. Ağaç türleri bakımından değerlendirildiğinde en küçük ?E*, MSBV sistemi uygulanmış yüzeylerde olduğu belirlenmiştir. Pandüllü sertlik değerlerinde ise vernik türünde en küçük NSBV sisteminde 86.33, en yüksek NSBV + QUV kombinasyonunda 96.55 olarak belirlenirken; MSBV + QUV’da 96.22, MSBV kombinasyonunda 95.61; ağaç türünde (kaplama çeşidi) en yüksek meşe + MSBV + QUV varyasyonunda 107.00, en düşük Okaliptüs + MSBV’de 87.33 şeklinde gerçekleşmiştir.