Yazar "Akkuş, Memiş" seçeneğine göre listele

Listeleniyor 1 - 6 / 6
  • Küçük Resim
    Öğe
    Analysis of Usability in Furniture Production of Wood Plastic Laminated Board
    (North Carolina State Univ Dept Wood & Paper Sci, 2015) İlçe, Abdullah Cemil; Budakçı, Mehmet; Özdemir, Serkan; Akkuş, Memiş
    The objective of this study was to manufacture a lightweight and easily producible wood plastic laminate (WPL) board that could be used in the furniture sector. Eastern beech (Fagus orientalis L.) veneer papels (A) and hollow polycarbonate boards (B), both with a thickness of 4 mm, were laminated in different combinations using polyurethane (PUR) and polychloroprene (PCR) adhesives. The physical and mechanical properties of the WPL boards obtained were determined according to the principles specified in the EN 326-1, EN 317, EN 310, ASTM D1037, and ASTM D1761 standards. Subsequently, the specimens were compared with particle boards (PB), medium density fiberboards (MDF), and okoume plywoods (PW). According to the results, the AABAA, ABABA, and ABBBA combinations of the WPL materials had better physical properties, such as weight, water absorption, and swelling thickness, compared to the other composites. Furthermore, because the WPL materials had a high bending resistance, modulus of elasticity, and nail and screw withdrawal strength, they could be used instead of PB and MDF. The WPL material obtained within the scope of this study are suitable for furniture making.
  • Küçük Resim
    Öğe
    Application of Electrostatic Powder Coating on Wood Composite Panels Using a Cooling Method. Part 1: Investigation of Water Intake, Abrasion, Scratch Resistance, and Adhesion Strength
    (North Carolina State Univ Dept Wood & Paper Sci, 2019) Akkuş, Memiş; Akbulut, Turgay; Candan, Zeki
    Powder coating is environmentally friendly and safe in terms of human health and is used especially on home appliances and in the automotive sector. Because of these advantages, recent studies have expanded work on the application of powder coating on non-conductive surfaces. Within the scope of this research, low temperature curing (120 degrees C to 130 degrees C) was applied on wood-based composite panels of medium-density fiberboard (MDF), particleboard, and plywood to facilitate conductivity. Epoxy, polyester, and hybrid (epoxy-polyester) types of powder paint and water-based liquid paint (control group) were applied to the surface of materials. Panels coated with the powder coatings were compared to the panels coated with the water-soluble acrylic resin coating. The prepared samples were analyzed for performance properties. The best results for thickness swelling, water absorption, adhesive strength, abrasion, and scratch resistance were found for the plywood coated with water-based liquid paint, MDF coated with polyester-based powder paint, plywood coated with hybrid powder paint, particleboard coated with hybrid powder paint, and plywood coated with epoxy powder paint, respectively.
  • Küçük Resim
    Öğe
    Effect of Thermal Modification on the Surface Quality of a Coating Applied to Wood via the Electrostatic Spray Deposition Technique
    (North Carolina State Univ Dept Wood & Paper Sci, 2021) Ayrılmış, Nadir; Akkuş, Memiş; Yılmaz, Sena Nur
    The surface properties of thermally modified ash wood with a powder coating were investigated, and the results were compared to the unmodified wood. The wood specimens were sanded with 80 grit sandpaper and then pre-heated at 80 degrees C for 5 min in an infrared oven. The surface of the unmodified and the modified wood specimens were coated with an epoxy/polyester (1 to 1 ratio) hybrid coating using an electrostatic corona spray gun at the pilot plant established in the laboratory. The coatings on the wood specimens were cured at different curing conditions in an infrared oven, i.e., 120 degrees C/15 min, 140 degrees C/10 min, and 160 degrees C/10 min. The results showed that the thermal modification (TM) of the wood caused a slight decrease in the mechanical performance of the surface system (wood substrate and coating film). For example, the scratch and abrasion resistance of the unmodified specimens at the curing temperature of 120 degrees C were 3.33 N and 135 revolutions but were 3.12 N and 120 revolutions after the TM. However, the average surface roughness (1.26 mu) and contact angle (60.8 degrees) of the distilled water on the cured coatings on the modified wood were lower than those on the unmodified wood (1.86 mu and 80.8 degrees, respectively).
  • Küçük Resim
    Öğe
    EFFECTS OF THERMAL AGING ON THE FILM HARDNESS OF SOME WOOD VARNISHES
    (North Carolina State Univ Dept Wood & Paper Sci, 2011) Sönmez, Abdullah; Budakçı, Mehmet; Demirci, Zafer; Akkuş, Memiş
    This study was performed to determine the effects of thermal aging on the film hardness of some wood varnishes. For this purpose, Scots pine (Pinus sylvestris L.), Eastern beech (Fagus orientalis L.), and oak (Quercus petraea L.) samples coated with synthetic (alkyd), two-part polyurethane (urethane-alkyd), and waterborne (self cross-linked polyurethane) varnishes were evaluated at a moisture content of 8% and 12%. Afterwards, thermal aging processes were performed for periods of 25, 50, 75, and 100 days at 25 degrees C, 50 degrees C, 75 degrees C, and 100 degrees C. Hardness changes in the varnish films were measured in accordance with ISO 1522-2006. According to the test results, the samples prepared with polyurethane varnishes at 8% moisture content give the best results.
  • Küçük Resim
    Öğe
    Elektrostatik toz boya uygulanmış ahşap esaslı levhaların bazı teknolojik özelliklerinin incelenmesi
    (2021) Akkuş, Memiş
    Elektrostatik toz boyalar, otomotiv ve beyaz eşya gibi iletken metalik yüzeyler üzerine uygulanmaktadır. Elektrostatik toz boyalar uçucu organik bileşik içermemesi, çevre, iş güvenliği ve işçi sağlığı açısından diğer sıvı boyalara göre daha avantajlıdır. Bu avantajlarından dolayı son zamanlarda iletken olmayan plastik, ahşap ve ahşap esaslı levhalara uygulanması yönünde birçok araştırma ve geliştirme faaliyetleri yürütülmektedir. Bu çalışmada ahşap esaslı levhalardan yongalevha ve orta yoğunlukta liflevha (MDF) yüzeylerinin iletkenlik değerini artırmak için ön ısıtma (70 °C) ve sonrasında korona tipi tabanca ile hibrit esaslı (Epoksi/Polyester) elektrostatik toz boya işlemi uygulanmıştır. Daha sonra örnekler, kızılötesi (infarared) fırınlarda 130 °C sıcaklıkta 20 dakika boyunca kürlenme işlemine tabi tutulmuştur. Ön ısıtma ve kürlenme esnasında MDF ve yongalevhalarda ısının etkisi ile levhalarda mekanik ve fiziksel değişimler öngörülmektedir. Bu amaç doğrultusunda; elektrostatik toz boya uygulanmış ve uygulanmamış MDF ve yongalevha örneklerinin, TS 319 standardına göre iç yapışma direnci, TS EN 310 standardına göre eğilme direnci, TS EN 320 standardına göre vida çekme direnci, ASTM D 1037 standardına göre su alma oranı ve TS EN 317 standardına göre kalınlığına şişme testlerine tabi tutularak istatistiksel karşılaştırılması yapılmıştır. Yapılan karşılaştırma sonucunda, elektrostatik toz boya ile kaplanması MDF örneklerinde çok fazla değişikliğe neden olmaz iken, yongalevha örneklerinin mekanik ve fiziksel özelliklerini etkilediği tespit edilmiştir.
  • Küçük Resim
    Öğe
    Renk açma işleminin termal modifikasyon yapılmış bazı ağaç malzemelere etkisi
    (Düzce Üniversitesi, 2012) Akkuş, Memiş; Budakçı, Mehmet
    Bu çalışmanın amacı, renk açma işleminin termal modifikasyon yapılmış bazı ağaç malzemelere etkisini belirlemektir. Bu amaçla ısıl işlem sonrası ağaç malzemede meydana gelen bazı fiziksel bozunmaları gidermek için çeşitli renk açma kimyasalları kullanarak, malzemenin doğal renk, parlaklık ve sertlik değerleri elde edilmeye çalışılmıştır. Sarıçam (Pinus Sylvestris L.), Sapsız meşe (Quercus petraea L.), Doğu kayın (Fagus Orientalis L.) ve göknar (Abies Bornmülleriana Mattf.) odunlarından hazırlanan örnekler, farklı sıcaklıklarda (140?1600C) ve farklı zaman (3-5-7 saat) periyotlarında ısıl işleme tabi tutulmuştur. Daha sonra malzeme yüzeylerine % 18 konsantrasyondaki renk açma çözeltileri Ç1 (NaOH + H2O2), Ç2 (NaSiO3 + H2O2) ve Ç3 (H2C2O4) uygulanarak, oluşan renk, parlaklık ve sertlik değişim değerleri, ASTM D 2224, EN ISO 2813 ve ASTM D 2240 standartlarına göre belirlenmiştir. Araştırma sonucuna göre; kullanılan renk açma çözeltileri ısıl işlem görmüş ağaç malzeme yüzeylerinde, renk ve parlaklık değerlerinde azalma, sertlik değerinde ise artışa yol açmıştır. Buna göre; ısıl işlem görmüş ağaç malzeme yüzeylerinde doğal renk, parlaklık ve sertlik değerlerine yakın sonuçlar elde edebilmek için Ç1 ve Ç2 çözelti grubları tercih edilmesi önerilebilir.